产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 熔体流动速率 | 200℃5kg | ASTM D-1238 | 0.6 | g/10min |
| 比重 | ASTM D-792 | 1.03 | 23/23℃ | |
| 燃烧率 | File No. E56070 ULC-UL | 1/16HB | ||
| 熔体流动速率 | 220℃10kg | ASTM D-1238 | 6 | g/10min |
| 弯曲强度 | ASTM D-790 | 9070 | lb/in2 | |
| 弯曲强度 | ASTM D-790 | 640 | kg/cm2 | |
| 弯曲弹性率 | ASTM D-790 | 3.2105 | lb/in2 | |
| IZOD冲击强度 | 1/4 | ASTM D-256 | 40 | kg.cm/cm |
| IZOD冲击强度 | 1/8 | ASTM D-256 | 45 | kg.cm/cm |
| 洛氏硬度 | ASTM D-785 | 102 | R | |
| IZOD冲击强度 | 1/4 | ASTM D-256 | 7.4 | ft.lb/in |
| 引张强度 | ASTM D-638 | 400 | kg/cm2 | |
| IZOD冲击强度 | 1/8 | ASTM D-256 | 8.4 | ft.lb/in |
| 伸长率 | ASTM D-638 | 40 | % | |
| 引张强度 | ASTM D-638 | 5670 | lb/in2 | |
| 弯曲弹性率 | ASTM D-790 | 2.3104 | kg/cm2 | |
| 维卡软化点 | ASTM D-1525 | 105 | ℃ | |
| 维卡软化点 | ASTM D-1525 | 221 | ℉ | |
| 热变形温度 | ASTM D-648 | 88(190) | ℉ | |
| 热变形温度 | ASTM D-648 | 98(208) | ℃ |